Sintered cubic boron nitride compact and sintered cubic boron nitride compact tool

ABSTRACT

It is an object of the present invention to provide a sintered cBN compact having excellent wear resistance and fracture resistance even in machining centrifugally cast iron having a property of being difficult to machine, and to provide a sintered cBN compact tool. A sintered cBN compact of the present invention contains 20% by volume or more and 65% by volume or less of cBN and, as a binder, 34% by volume or more and less than 80% by volume of Al 2 O 3 , at least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof (hereinafter, referred to as “X”), and ZrO 2 , the total amount of X and ZrO 2  being 1.0% by volume or more and 6.0% by volume or less, the volume ratio of ZrO 2  to Al 2 O 3 , ZrO 2 /Al 2 O 3 , being 0.010 or more and less than 0.100, in which the ratio I tetragonal ZrO2 (101)/I αAl2O3 (110) is 0.1 or more and 3 or less, where I tetragonal ZrO2 (101) is the intensity of the (101) plane of tetragonal ZrO 2  and I αAl2O3 (110) is the intensity of the (110) plane of αAl 2 O 3  among X-ray diffraction peaks of the sintered cBN compact.

TECHNICAL FIELD

The present invention relates to a sintered cubic boron nitride compact (sintered cBN compact) having excellent wear resistance and fracture resistance, and to a sintered compact tool using the same. More particularly, the invention relates to a sintered cubic boron nitride compact having excellent wear resistance and fracture resistance and serving as a cutting tool for centrifugally cast iron.

BACKGROUND ART

In recent years, there has been a tendency for the material used to form cylinder blocks to shift from cast iron to aluminum in order to reduce the weight of engines, and cast iron produced by a centrifugal casting process has been increasingly employed as cylinder liners in the blocks.

Centrifugally cast iron has low machinability compared to common cast iron produced using sand molds, and the life of tools used for cutting centrifugally cast iron is noticeably short, which is a problem.

Since centrifugally cast iron has fine, dense A-type structures, which are also observed in conventional sand mold cast iron, wear of a cutting tool is significantly increased by thermal reaction with a workpiece, resulting in a marked decrease in machinability of centrifugally cast iron.

It is known that a sintered cBN compact to which Al₂O₃ having excellent oxidation resistance and chemical stability has been added is effective as a cutting tool in order to machine such centrifugally cast iron having a property of being difficult to machine. However, the toughness and sinterability of a sintered cBN compact to which Al₂O₃ has been added are low. In order to overcome this problem, Patent Literatures 1 and 2 each disclose a sintered cBN compact whose fracture resistance is improved by addition of ZrO₂ to Al₂O₃.

For example, Patent Literature 1 discloses a sintered cBN compact including Al₂O₃, TiC or TiCN, and ZrO₂, in which the sintered cBN compact is produced using a starting material containing 50% by volume or more and 80% by volume or less of the cBN component, 1% by volume or more and 20% by volume or less of TiC or 0.5% by volume or more and 15% by volume or less of TiCN, and 15% by volume or more and 50% by volume or less of Al₂O₃ and ZrO₂, the ZrO₂/Al₂O₃ ratio by weight being 0.1 or more and 4 or less. When the ratio by weight specified by ZrO₂/Al₂O₃ is converted to a ratio by volume, 0.065≦ZrO₂/Al₂O₃≦2.62.

Furthermore, Patent Literature 2 discloses a material for a sintered compact having a composition including 40% to 70% by volume of cBN powder particles, 15% to 45% by volume of titanium nitride serving as a major component of a binder phase and 15% to 35% by volume of mixed powder particles of Al₂O₃, ZrO₂, AlN, and acicular crystals of SiC serving as an accessory component of the binder phase, in which the accessory component of the binder phase is composed of 50% to 65% by volume of Al₂O₃, 1% to 5% by volume of ZrO₂, 20% to 40% by volume of AlN, and 5% to 15% by volume of acicular crystals of SiC.

In a centrifugal casting process, by pouring molten cast iron into a rotating cylindrical mold, it is possible to produce a thin sleeve, which is advantageous. However, since a portion of the sleeve in contact with the mold and a portion of the sleeve located at the inner diameter surface are rapidly cooled, the cast iron structure is refined, resulting in generation of abnormal structures, such as dendritic structures and rosette structures. These abnormal structures, such as dendritic structures and rosette structures, have very poor machinability. In most recent sleeves made of centrifugally cast iron, the thickness has been decreased in order to shorten the distance between cylinder bores, and it has become necessary to cut, in addition to fine, dense A-type structures which are regions to be cut in conventional centrifugally cast iron, regions where rosette structures and dendritic structures exist, which are not regions to be cut in conventional centrifugally cast iron. When regions where rosette structures and dendritic structures exist are subjected to cutting, machining is required to be carried out under thermally harsh conditions compared with conventional centrifugally cast iron, and therefore, machinability is markedly decreased, which is a problem.

When such centrifugally cast iron is machined using the sintered compact described in any of the above-mentioned Patent Literatures, since a large amount of ZrO₂ having very low thermal conductivity compared to Al₂O₃ is contained, the thermal conductivity of the sintered compact decreases, and reaction with the workpiece under machining proceeds markedly, resulting in a significant decrease in wear resistance.

CITATION LIST Patent Literature

PTL 1: International Publication No. 2008/087940

PTL 2: Japanese Patent No. 2971203

SUMMARY OF INVENTION Technical Problem

It is an object of the present invention to provide a sintered cBN compact having excellent wear resistance and fracture resistance even in machining centrifugally cast iron having a property of being difficult to machine and having, in addition to, the fine, dense A-type structures, rosette structures and dendritic structures, and to provide a sintered cBN compact tool.

Solution to Problem

The present inventors have performed thorough studies and have found that, in a sintered cBN compact, by adding, as a binder, Al₂O₃, ZrO₂, and at least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof, the X-ray diffraction intensity of ZrO₂ changes. Furthermore, it has been found that the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) correlates with cutting performance and sinterability. Furthermore, it has been found that, by setting the volume ratio of ZrO₂ to Al₂O₃ in the sintered cBN compact and the numerical value of the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) within specified ranges, both wear resistance and fracture resistance can be markedly improved. Thus, the present invention has been achieved.

That is, the present invention is as described below.

-   -   (1) A sintered cBN compact containing 20% by volume or more and         65% by volume or less of cBN relative to the whole sintered         compact and, as a binder, 34% by volume or more and less than         80% by volume of Al₂O₃ relative to the whole sintered compact,         at least one selected from the group consisting of nitrides,         carbides, carbonitrides, borides, and boronitrides of Zr and         solid solutions thereof (hereinafter, referred to as “X”), and         ZrO₂, the total amount of X and ZrO₂ being 1.0% by volume or         more and 6.0% by volume or less relative to the whole sintered         compact, the volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃, being         0.010 or more and less than 0.100, characterized in that the         ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.1 or more         and 3 or less, where I_(tetragonal ZrO2)(101) is the intensity         of the (101) plane of tetragonal ZrO₂ and I_(αAl2O3)(110) is the         intensity of the (110) plane of αAl₂O₃ among X-ray diffraction         peaks of the sintered cBN compact.     -   (2) The sintered cBN compact according to (1) described above,         characterized by containing ZrC as the X.     -   (3) The sintered cBN compact according to (1) or (2) described         above, characterized in that the ratio         I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.2 or more and 0.5         or less.     -   (4) A sintered cBN compact tool characterized by including the         sintered cBN compact according to any one of (1) to (3)         described above at least at an edge portion thereof.

Advantageous Effects of Invention

According to the present invention, it is possible to obtain a sintered cBN compact having excellent wear resistance and fracture resistance, which is useful as a cutting tool used for machining a difficult-to-machine workpiece, such as centrifugally cast iron having, in addition to, fine, dense A-type structures, rosette structures and dendritic structures.

DESCRIPTION OF EMBODIMENTS

A sintered cBN compact of the present invention contains 20% by volume or more and 65% by volume or less of cBN relative to the whole sintered compact and, as a binder, 34% by volume or more and less than 80% by volume of Al₂O₃ relative to the whole sintered compact, at least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof (hereinafter, referred to as “X”), and ZrO₂, the total amount of X and ZrO₂ being 1.0% by volume or more and 6.0% by volume or less, the volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃, being 0.010 or more and less than 0.100. The sintered cBN compact is characterized in that the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.1 or more and 3 or less, where I_(tetragonal ZrO2)(101) is the intensity of the (101) plane of tetragonal ZrO₂ and I_(αAl2O3)(110) is the intensity of the (110) plane of αAl₂O₃ among X-ray diffraction peaks of the sintered cBN compact.

In this case, the cBN content in the sintered compact is 20% by volume or more and 65% by volume or less, and preferably 40% by volume or more and 50% by volume or less, relative to the whole sintered compact. When the cBN component content is less than 20% by volume, strength is insufficient for cutting difficult-to-machine centrifugally cast iron, and fracture resistance is decreased, resulting in fracturing of edge. On the other hand, when the content exceeds 65% by volume, since the Al₂O₃ content relatively decreases, heat resistance is decreased. As a result, a reaction is likely to be caused by heat generated during cutting, and wear is likely to increase.

Furthermore, in the present invention, the composition of the individual components relative to the whole sintered compact, which can be measured, for example, as described below, is the same as that of the starting materials used and does not change.

Regarding the composition of the individual components, first, a sintered cBN compact was subjected to mirror polishing, and the structure in a given region was photographed as a backscattered electron image of a scanning electron microscope with a magnification of 10,000 times. Three gradations of light and shade contrast corresponding to the composition were observed in the photograph taken. An analysis with an energy dispersive X-ray analyzer (EDX) in the same field of view at the same time revealed that darkest portions in the observed field corresponded to cBN particles, middle-toned portions corresponded to Al₂O₃ particles, and lightest portions corresponded to Zr compounds (oxides, carbides, nitrides, borides, and boronitrides). By subjecting the backscattered electron image to image analysis, the contents by volume of the individual components were determined

Furthermore, the composition of the Zr compounds was measured by chemical analysis, such as plasma emission spectroscopic analysis (ICP) or gas analysis.

A description will now be made on a binder.

A sintered cBN compact of the present invention contains Al₂O₃ in the amount of 34% by volume or more and less than 80% by volume, preferably 50% by volume or more and 60% by volume or less, relative to the whole sintered compact. When the Al₂O₃ content is less than 34% by volume, wear resistance is decreased. When the Al₂O₃ content is 80% by volume or more, fracture resistance is decreased.

By incorporating Al₂O₃, it is possible to prevent an increase of wear due to a reaction between cast iron and the edge components by using properties, such as oxidation resistance and chemical stability, of Al₂O₃. However, in a system containing a large amount of Al₂O₃, pores are likely to be generated in the surface of cBN, resulting in decreases in sinterability and fracture resistance.

Furthermore, Al₂O₃ has high heat resistance, but lacks in toughness. Therefore, incorporation of Al₂O₃ only causes easy occurrence of chipping in the edge. By incorporating at least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof (hereinafter, referred to as “X”) which easily reacts with cBN and markedly improves thermal conductivity in the binder, and ZrO₂ which is effective in improving toughness of Al₂O₃, it is possible to markedly improve both fracture resistance and wear resistance.

At least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof (hereinafter, referred to as “X”) and ZrO₂ are contained in the sintered cBN compact, in total, in the amount of 1.0% by volume or more and 6.0% by volume or less relative to the whole sintered compact, and the volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃, is 0.010 or more and less than 0.100.

By incorporating X and ZrO₂, in total, in the amount of 1.0% by volume or more and 6.0% by volume or less, fracture resistance is improved. The total amount of X and ZrO₂ is more preferably more than 2.5% by volume and 4.0% by volume or less, by which wear resistance is further improved.

Furthermore, by setting the volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃ to be 0.010 or more and less than 0.100, wear resistance and fracture resistance can be improved. When the ratio ZrO₂/Al₂O₃ is less than 0.010, it is not possible to obtain the effect of improving toughness of Al₂O₃ by ZrO₂, resulting in a decrease in fracture resistance. When the ratio is 0.100 or more, wear resistance is decreased. The volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃ is more preferably 0.02 or more and less than 0.06.

Furthermore, when the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.1 or more and 3 or less, where I_(tetragonal ZrO2)(101) is the intensity of the (101) plane of tetragonal ZrO₂ and I_(αAl2O3)(110) is the intensity of the (110) plane of αAl₂O₃ among X-ray diffraction peaks of the sintered cBN compact measured by an X-ray diffractometer (Cu used for X-ray tube), sinterability is increased, and a dense sintered compact can be obtained. Therefore, the sintered compact has excellent fracture resistance and wear resistance, and also the yield of the sintered compact is markedly improved, thus contributing to a reduction in costs. When the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is less than 0.1, the effect of improving sinterability cannot be obtained. When the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) exceeds 3, wear resistance is decreased. The ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is more preferably 0.2 or more and 0.5 or less.

In particular, by incorporating ZrC as X, the peak intensity of tetragonal ZrO₂(101) can be selectively increased. Even when the Al₂O₃ content is relatively increased by a small amount of ZrC, the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) can be 0.2 or more and 0.5 or less, resulting in improvement in sinterability, fracture resistance, and productivity. Preferably, the content of ZrC in the sintered cBN compact is 0.1% by volume or more and 3.0% by volume or less.

A sintered compact of the present invention can be obtained by sintering the starting materials for the sintered compact.

For example, first, Al₂O₃, ZrO₂, and X are pulverized and mixed in advance to produce a binder. Then, mixed powder obtained by homogeneously mixing cBN particles and the binder is sintered under ultrahigh pressure conditions (5.5 to 7 GPa, 1,300° C. to 1,800° C.). Thereby, a sintered cBN compact of the present invention can be produced.

The volume-average particle size of Al₂O₃ used as the binder is preferably 1 μm or less, and more preferably 50 to 500 nm. Furthermore, the volume-average particle size of each of X and ZrO₂ used as the binder is preferably 1 μm or less, and more preferably 10 to 100 nm.

As a sintered cBN compact tool of the present invention, a sintered cBN compact tool including a sintered cBN compact at least at an edge portion of a substrate made of cemented carbide, or a sintered cBN compact tool composed of a sintered cBN compact only may be mentioned. These can be produced in accordance with a known method. Furthermore, the sintered cBN compact may have a hard ceramic coating layer on the surface thereof.

EXAMPLES

An example of an embodiment of the present invention will be described below on the basis of Examples. It is to be understood that Examples below are merely illustrative and do not limit the present invention.

Example 1

Al₂O₃ with a volume-average particle size of 1 μm or less, ZrO₂ with a volume-average particle size of 0.5 μm or less, and a Zr compound with a volume-average particle size of 1 μm or less were used, with the composition shown in Table. The compounds were mixed and pulverized in advance with ZrO₂ ball media having a diameter of 0.6 mm in an ethanol solvent at a flow rate of 0.6 L/min for 150 minutes. Then, by removing the media, a special binder in which Zr compound ultrafine particles were homogeneously dispersed in Al₂O₃ was produced. The volume-average particle size of Al₂O₃ was 250 nm, and the volume-average particle size of X and ZrO₂ was 50 nm after mixing and pulverization.

Mixed powder, which was obtained by homogeneously mixing cBN particles (volume-average particle size: 2 μm) having the composition shown in Table and the binder by a ball mill mixing method using ZrO₂ ball media having a diameter of 3 mm, was stacked on a support plate made of cemented carbide and placed in a capsule made of Mo. Then, by performing sintering with an ultrahigh-pressure apparatus at a pressure of 6.5 GPa and a temperature of 1,700° C. for 30 minutes, a sintered compact was produced. Compounds were identified by X-ray diffraction measurement, and the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) was calculated.

Examples 2 to 10 and Comparative Examples 1 to 5

Sintered cBN compacts were produced as in Example 1 except that the composition and compounds of starting materials for sintered compacts were changed to those shown in Table.

Evaluation

The resulting sintered compacts were processed into cutting inserts complying with ISO standard SNGN090312, and a continuous cutting test (inner diameter) was conducted.

A centrifugally cast iron sleeve with an inner diameter of 85 mm was turned at a cutting speed of 700 m/min, with a depth of cut of 0.3 mm, and with a feed of 0.05 mm/rev, using wet cutting [coolant: emulsion (manufactured by Japan Fluid System, trade name: System Cut 96) diluted 20 times]. The flank wear amount after cutting 1 km and the edge state after cutting 2 km (presence or absence of flank wear and chipping) were checked.

The results thereof are shown in Table.

In all of the sintered cBN compacts of Examples, a normal polished surface is obtained. In contrast, in Comparative Examples 1 and 2 in which X is not contained, very small falling-off of the sintered compact is observed, which is caused by insufficient sintering.

When Examples 1 to 4 are compared, in Example 3 in which the cBN content is in the range of 40% to 50% by volume, the wear amount is smallest and good results are obtained.

In Examples 1 to 10 in which the X+ZrO₂ value is in the range 1.0% to 6.0% by volume, the wear amount is markedly small compared with Comparative Example 3 in which the same value is 10.0% by volume, and good results are obtained. Furthermore, in Example 3 in which the same value is in the range of 2.5% to 4.0% by volume, the ratio ZrO₂/Al₂O₃ is in the range of 0.02 to 0.06, and the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is in the range of 0.2 to 0.5, the wear amount is smallest, fracturing and chipping do not occur, and the best results are obtained.

In Comparative Example 4 in which the ratio ZrO₂/Al₂O₃ is 0.125 and the ratio I_(tetragonal ZrO2)(101)/I_(Al2O3)(110) is 5.8, the wear amount is markedly large compared with Examples 1 to 10 because the wear resistance of ZrO₂ is markedly lower than that of Al₂O₃, and it is assumed that at the point of 2 km, the cutting force is increased by the large wear amount, resulting in fracturing.

In Comparative Example 5, in which the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.05, it is assumed that wear resistance and fracture resistance are decreased because of insufficient sintering.

TABLE ZrO2/Al₂O₃ Wear amount Edge cBN Al₂O₃ ZrO2 X ZrO2 + X (volume I_(tetragonalZrO2)(101)/ after cutting state after (vol %) Starting material (vol %) (vol %) (vol %) (vol %) ratio) I_(αAl2O3)(110) 1 km (μm) cutting 2 km Example 1 20 cBN, Al2O3, ZrO2, 77.9 1.6 0.5 2.1 0.021 0.8 82 Very small ZrC chipping Example 2 32 cBN, Al2O3, ZrO2, 65.5 1.0 1.5 2.5 0.015 0.4 72 Normal wear ZrC Example 3 45 cBN, Al2O3, ZrO2, 52.3 1.2 1.5 2.7 0.023 0.4 61 Normal wear ZrC Example 4 65 cBN, Al2O3, ZrO2, 34 0.5 0.5 1.0 0.015 0.5 92 Large wear ZrC Example 5 45 cBN, Al2O3, ZrO2, 51 3.0 1.0 4.0 0.059 1.9 78 Very small ZrN chipping Example 6 45 cBN, Al2O3, ZrO2, 49 4.5 1.5 6.0 0.092 3.0 81 Normal wear ZrB2 Example 7 45 cBN, Al2O3, ZrO2, 49.5 3.0 2.5 5.5 0.061 1.5 92 Very small Zr5B2N2 chipping Example 8 45 cBN, Al2O3, ZrO2, 51.7 1.8 1.5 3.3 0.035 0.6 70 Normal wear ZrC Example 9 45 cBN, Al2O3, ZrO2, 52.9 0.6 1.5 2.1 0.011 0.2 67 Chipping ZrC Example 10 45 cBN, Al2O3, ZrO2, 50 2.0 3.0 5.0 0.040 2.5 75 Very small ZrCN chipping Comparative 45 cBN, Al2O3, ZrO2 52 3.0 0 3.0 0.058 0.1 154 Fracturing Example 1 Comparative 45 cBN, Al2O3 55 0 0 0 0.000 0.0 182 Fracturing Example 2 Comparative 45 cBN, Al2O3, ZrO2, 45 2.0 8.0 10.0 0.044 1.2 137 Fracturing Example 3 ZrC Comparative 50 cBN, Al2O3, ZrO2, 44 5.5 0.5 6.0 0.125 5.8 139 Fracturing Example 4 ZrC Comparative 40 cBN, Al2O3, ZrO2, 54.2 0.8 5.0 5.8 0.015 0.05 132 Fracturing Example 5 ZrB2

INDUSTRIAL APPLICABILITY

A sintered cBN compact of the present invention has excellent wear resistance and fracture resistance, and is useful as a cutting tool used for machining a difficult-to-machine workpiece, such as centrifugally cast iron having, in addition to, fine, dense A-type structures, rosette structures and dendritic structures. 

1. A sintered cBN compact, containing: 20% by volume or more and 65% by volume or less of cBN relative to the whole sintered compact; and as a binder, 34% by volume or more and less than 80% by volume of Al₂O₃ relative to the whole sintered compact, at least one selected from the group consisting of nitrides, carbides, carbonitrides, borides, and boronitrides of Zr and solid solutions thereof (hereinafter, referred to as “X”); and ZrO₂, wherein the total amount of X and ZrO₂ being 1.0% by volume or more and 6.0% by volume or less relative to the whole sintered compact, the volume ratio of ZrO₂ to Al₂O₃, ZrO₂/Al₂O₃, being 0.010 or more and less than 0.100; and wherein the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.1 or more and 3 or less, where I_(tetragonal ZrO2)(101) is the intensity of the (101) plane of tetragonal ZrO₂ and I_(αAl2O3)(110) is the intensity of the (110) plane of αAl₂O₃ among X-ray diffraction peaks of the sintered cBN compact.
 2. The sintered cBN compact according to claim 1, wherein the sintered cBN compact containing ZrC as the X.
 3. The sintered cBN compact according to claim 1, wherein the ratio I_(tetragonal ZrO2)(101)/I_(αAl2O3)(110) is 0.2 or more and 0.5 or less.
 4. A sintered cBN compact tool comprising the sintered cBN compact according to claim 1 at least at an edge portion thereof.
 5. The sintered cBN compact according to claim 2, wherein the ratio I_(tetragonal ZrO2)(101)/I_(Al2O3)(110) is 0.2 or more and 0.5 or less.
 6. A sintered cBN compact tool comprising the sintered cBN compact according to claim 2 at least at an edge portion thereof.
 7. A sintered cBN compact tool comprising the sintered cBN compact according to claim 3 at least at an edge portion thereof.
 8. A sintered cBN compact tool comprising the sintered cBN compact according to claim 5 at least at an edge portion thereof. 